PVB Resina pro PVB Interlayer et Alia Applications

Polyvinyl resina butyralis fit ex PVA et butyraldehyde sub acido catalysi.Cum notis bonae cinematographicae formationis, adhaesionis, tempestatis resistentiae et solubilitatis, PVB resina locum habet pro PVB interposito et electronicis ceramicis, coatings, inks.


Product Image

2121

Applications

Gradus

Flavo Test

Volatile

substantia

content(%)

Hydroxyl

content(%)

Coetus acetalis

Content (%)

Obducto

Lux Transmittance

Confluat Index @120℃

(g/10min)

liberum acidum

Content (%)

Viscositas (100% PVB solutio) mPa.s

mole Density

(g/100mL)

PVB Interlayer

DVB201

Non visual flavo-

1.5

17.0~20.0

75-80

≤0.40

≥87.0

0.90 -1.70

≤0.0100

1000~1400

≥ 14.0

DVB202

Non visual flavo-

1.5

17.0~20.0

75-80

≤0.40

≥87.0

1.30 -2.10

≤0.0100

9001300

≥ 14.0

Electronic tellus, membrana, atramentum

Gradus

Volatile

substantia

content(%)

Butyl

aldehyde

content(wt%)

Hydroxyl

content(wt%)

liberum acidum

Content (%)

Viscositas

23℃(mPa.s)

DVB402

3.0

76.0 ~ 80.0

18.0 ~ 21.0

0.50

10~ 30

DVB412

3.0

76.0 ~ 80.0

18.0 ~ 21.0

0.50

30~ 50

DVB413

3.0

71.0 ~74.0

24.0 ~ 27.0

0.50

10~ 60

DVB422

3.0

76.0 ~ 80.0

18.0 ~ 21.0

0.50

50~ 80

DVB432

3.0

76.0 ~ 80.0

18.0 ~ 21.0

0.50

100~ 170

DVB433

3.0

71.0 ~74.0

24.0 ~ 27.0

0.50

140~ 220

DVB462

3.0

76.0 ~ 80.0

18.0 ~ 21.0

0.50

40~ 90*

DVB463

3.0

71.0 ~74.0

24.0 ~ 27.0

0.50

60~ 120*

*in 5%ethanol praeservatum solution, alii in X%ethanol praeservatum solution